Tribological Behavior and Wear Mechanisms of Powder Metallurgy Copper-Titanium Dioxide Composites under Dry Sliding Conditions
Keywords:
Copper matrix composites, Titanium dioxide, Tribology, Wear mechanisms, Powder metallurgy, Dry slidingAbstract
This research analyzes the tribological properties and wear mechanisms of copper-titanium dioxide (Cu-TiO₂) metal matrix composites developed using powder metallurgy subjected to dry sliding conditions. Cu-TiO₂ composites having TiO₂ nanoparticles of 0, 2, 4, 6, and 8 wt% were developed via mechanical mixing, cold compaction (300 MPa), and sintering (900°C in hydrogen) and tested tribologically comparing against hardened steel (EN31) counterface using a pin-on-disk tribometer at loads of 10, 20, 30N while sliding at velocities of 0.5, 1.0, 1.5m/s. Wear mechanisms were examined using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and surface profilometry. Results indicated that wear resistance was enhanced with TiO₂ additions, with the most favorable performance at 6 wt% TiO₂ loading. The wear rate decreased from 2.45 × 10⁻⁴ mm³/Nm for pure copper, to 0.68 × 10⁻⁴ mm³/Nm for Cu- 6wt%TiO₂ (72% improvement). The coefficient of friction decreased from 0.52 to 0.38 with increasing addition of TiO₂. Observations according to wear mechanisms determined that the severe adhesive and abrasive wear conditions experienced in the pure copper material evolved into mild oxidative wear when subjected to the TiO₂-reinforced composites. From the tests it was noted that a tribolayer formed which included TiO₂ particles and copper oxidizing compounds which had attributed positively to the tribological properties of the material. These results emphasize the potential of Cu-TiO₂ composites for improving wear resistance in sliding bearing and electrical contact applications.
References
K. H. Zum Gahr, Microstructure and Wear of Materials, Amsterdam: Elsevier, 1987.
G. W. Stachowiak and A. W. Batchelor, Engineering Tribology, 4th ed., Oxford: Butterworth-Heinemann, 2014.
K. Holmberg and A. Matthews, Coatings Tribology: Properties, Mechanisms, Techniques and Applications in Surface Engineering, 2nd ed., Amsterdam: Elsevier, 2009.
P. J. Blau, Friction Science and Technology: From Concepts to Applications, 2nd ed., Boca Raton: CRC Press, 2009.
I. M. Hutchings and P. Shipway, Tribology: Friction and Wear of Engineering Materials, 2nd ed., Oxford: Butterworth-Heinemann, 2017.
N. P. Suh, Tribophysics, Englewood Cliffs: Prentice-Hall, 1986.
R. Holm, Electric Contacts: Theory and Application, 4th ed., Berlin: Springer-Verlag, 1967.
V. V. Konchits, V. N. Pushkar, and I. V. Valitova, Electrical Contacts: Fundamentals, Applications and Technology, Boca Raton: CRC Press, 2007.
X. Chen and S. S. Mao, "Titanium dioxide nanomaterials: synthesis, properties, modifications, and applications," Chem. Rev., vol. 107, no. 7, pp. 2891-959, 2007.
U. Diebold, "The surface science of titanium dioxide," Surf. Sci. Rep., vol. 48, no. 5-8, pp. 53-229, 2003.
T. L. Thompson and J. T. Yates, "Surface science studies of the photoactivation of TiO2: new photochemical processes," Chem. Rev., vol. 106, no. 10, pp. 4428-53, 2006.
A. Erdemir, "A crystal chemical approach to the formulation of self-lubricating nanocomposite coatings," Surf. Coat. Technol., vol. 200, no. 5-6, pp. 1792-6, 2005.
Fujishima, X. Zhang, and D. A. Tryk, "TiO2 photocatalysis and related surface phenomena," Surf. Sci. Rep., vol. 63, no. 12, pp. 515-82, 2008.
R. M. German, Powder Metallurgy and Particulate Materials Processing, Princeton: Metal Powder Industries Federation, 2005.
M. Randall and R. M. German, Powder Metallurgy Science, 2nd ed., Princeton: Metal Powder Industries Federation, 1994.
E. Klar and P. K. Samal, Powder Metallurgy Stainless Steels: Processing, Microstructures, and Properties, Materials Park: ASM International, 2007.
D. A. Rigney, "Transfer, mixing and associated chemical and mechanical processes during the sliding of ductile materials," Wear, vol. 245, no. 1-2, pp. 1-9, 2000.
S. C. Tjong and Z. Y. Ma, "Microstructural and mechanical characteristics of in situ metal matrix composites," Mater. Sci. Eng. R, vol. 29, no. 3-4, pp. 49-113, 2000.
R. Casati and M. Vedani, "Metal matrix composites reinforced by nanoparticles: a review," Metals, vol. 4, no. 1, pp. 65-83, 2014.
D. B. Miracle, "Metal matrix composites: from science to technological significance," Compos. Sci. Technol., vol. 65, no. 15-16, pp. 2526-40, 2005.
N. Chawla and K. K. Chawla, Metal Matrix Composites, 2nd ed., New York: Springer, 2013.
D. J. Lloyd, "Particle reinforced aluminum and magnesium matrix composites," Int. Mater. Rev., vol. 39, no. 1, pp. 1-23, 1994.
D. A. Rigney and J. P. Hirth, "Plastic deformation and sliding friction of metals," Wear, vol. 53, no. 2, pp. 345-70, 1979.
P. Heilmann and D. A. Rigney, "An energy-based model of friction and its application to coated systems," Wear, vol. 72, no. 2, pp. 195-217, 1981.
T. F. J. Quinn, "Review of oxidational wear: Part I: The origins of oxidational wear," Tribol. Int., vol. 16, no. 5, pp. 257-71, 1983.
F. H. Stott, "High-temperature sliding wear of metals," Tribol. Int., vol. 35, no. 8, pp. 489-95, 2002.
S. C. Lim and M. F. Ashby, "Wear-mechanism maps," Acta Metall., vol. 35, no. 1, pp. 1-24, 1987.
J. F. Archard, "Contact and rubbing of flat surfaces," J. Appl. Phys., vol. 24, no. 8, pp. 981-8, 1953.
F. P. Bowden and D. Tabor, The Friction and Lubrication of Solids, Oxford: Oxford University Press, 2001.
J. A. Greenwood and J. B. P. Williamson, "Contact of nominally flat surfaces," Proc. R. Soc. Lond. A, vol. 295, no. 1442, pp. 300-19, 1966.
K. L. Johnson, Contact Mechanics, Cambridge: Cambridge University Press, 1985.
H. Blok, "Theoretical study of temperature rise at surfaces of actual contact under oiliness lubricating conditions," Proc. IME, vol. 2, pp. 222-35, 1937.
J. Jaeger, "Moving sources of heat and the temperature at sliding contacts," Proc. R. Soc. NSW, vol. 76, pp. 203-24, 1942.
A. Moghanian, F. Sharifianjazi, P. Abachi, E. Sadeghi, and H. Jafarikhorami, "Production and properties of Cu/TiO2 nano-composites," J. Alloys Compd., vol. 698, pp. 518-24, 2017.
Y. A. Sorkhe, H. Aghajani, and T. Taghizadeh Tabrizi, "Mechanical alloying and sintering of nanostructured TiO2 reinforced copper composite and its characterization," Mater. Des., vol. 58, pp. 168-74, 2014.
A. Rigney, "The roles of hardness in the sliding behavior of materials," Wear, vol. 175, no. 1-2, pp. 63-9, 1994.
M. Antler, "Processes of metal transfer and wear," Wear, vol. 7, no. 2, pp. 181-203, 1974.
H. Buckley, Surface Effects in Adhesion, Friction, Wear, and Lubrication, Amsterdam: Elsevier, 1981.
Rabinowicz, Friction and Wear of Materials, 2nd ed., New York: Wiley, 1995.
R. I. Trezona, D. N. Allsopp, and I. M. Hutchings, "Transitions between two-body and three-body abrasive wear: influence of test conditions in the microscale abrasive wear test," Wear, vol. 225-229, pp. 205-14, 1999.
T. F. J. Quinn, "Oxidational wear modelling: Part I. The general theory of oxidational wear," Wear, vol. 175, no. 1-2, pp. 199-208, 1994.
H. Stott and G. C. Wood, "The influence of oxides on the friction and wear of alloys," Tribol. Int., vol. 11, no. 4, pp. 211-8, 1978.
W. A. Glaeser, Materials for Tribology, Amsterdam: Elsevier, 1992.
E. Hornbogen, "The role of fracture toughness in the wear of metals," Wear, vol. 33, no. 2, pp. 251-9, 1975.
T. E. Fischer and H. Tomizawa, "Interaction of tribochemistry and microfracture in the friction and wear of silicon nitride," Wear, vol. 105, no. 1, pp. 29-45, 1985.
J. He and J. M. Schoenung, "Nanostructured coatings," Mater. Sci. Eng. A, vol. 336, no. 1-2, pp. 274-319, 2002.
A. T. Alpas and J. Zhang, "Effect of microstructure (particulate size and volume fraction) and counterface material on the sliding wear resistance of particulate-reinforced aluminum matrix composites," Metall. Mater. Trans. A, vol. 25, no. 5, pp. 969-83, 1994.
J. Zhang and A. T. Alpas, "Transition between mild and severe wear in aluminium alloys," Acta Mater., vol. 45, no. 2, pp. 513-28, 1997.
N. C. Welsh, "The dry wear of steels I: The general pattern of behaviour," Philos. Trans. R. Soc. Lond. A, vol. 257, no. 1077, pp. 31-50, 1965.
S. C. Lim, M. F. Ashby, and J. H. Brunton, "Wear-rate transitions and their relationship to wear mechanisms," Acta Metall., vol. 35, no. 6, pp. 1343-8, 1987.
Z. Zhang and D. L. Chen, "Consideration of Orowan strengthening effect in particulate-reinforced metal matrix nanocomposites," Scr. Mater., vol. 54, no. 7, pp. 1321-6, 2006.
V. C. Nardone and K. M. Prewo, "On the strength of discontinuous silicon carbide reinforced aluminum composites," Scr. Metall., vol. 20, no. 1, pp. 43-8, 1986.
P. J. Blau, "Elevated-temperature tribology of metallic materials," Tribol. Int., vol. 43, no. 7, pp. 1203-8, 2010.
H. Stott, "The role of oxidation in the wear of alloys," Tribol. Int., vol. 31, no. 1-3, pp. 61-71, 1998.
S. Wilson and A. T. Alpas, "Effect of temperature on the sliding wear performance of Al alloys and Al matrix composites," Wear, vol. 196, no. 1-2, pp. 270-8, 1996.
B. Venkataraman and G. Sundararajan, "The sliding wear behaviour of Al-SiC particulate composites: I. Macrobehaviour," Acta Mater., vol. 44, no. 2, pp. 451-60, 1996.
A. Wang and H. J. Rack, "Transition wear behavior of SiC-particulate- and SiC-whisker-reinforced 7091 Al metal matrix composites," Mater. Sci. Eng. A, vol. 147, no. 2, pp. 211-24, 1991.
S. C. Tjong, "Recent progress in the development and properties of novel metal matrix nanocomposites reinforced with carbon nanotubes and graphene nanosheets," Mater. Sci. Eng. R, vol. 74, no. 10, pp. 281-350, 2013.
J. Hashim, L. Looney, and M. S. J. Hashmi, "Particle distribution in cast metal matrix composites: Part I," J. Mater. Process. Technol., vol. 123, no. 2, pp. 251-7, 2002.
N. Hansen, "Hall-Petch relation and boundary strengthening," Scr. Mater., vol. 51, no. 8, pp. 801-6, 2004.
T. F. J. Quinn, "Review of oxidational wear: Part II: Recent developments and future trends in oxidational wear research," Tribol. Int., vol. 16, no. 6, pp. 305-15, 1983.
F. H. Stott and M. P. Jordan, "The effects of load and substrate hardness on the development and maintenance of wear-protective layers during sliding at elevated temperatures," Wear, vol. 250, no. 1-12, pp. 391-400, 2001.
A. Erdemir, "Review of engineered tribological interfaces for improved boundary lubrication," Tribol. Int., vol. 38, no. 3, pp. 249-56, 2005.
K. Miyoshi, Solid Lubrication Fundamentals and Applications, New York: Marcel Dekker, 2001.
B. Bhushan, Principles and Applications of Tribology, 2nd ed., New York: Wiley, 2013.
M. Braunovic, V. V. Konchits, and N. K. Myshkin, Electrical Contacts: Fundamentals, Applications and Technology, Boca Raton: CRC Press, 2007.
K. C. Ludema, Friction, Wear, Lubrication: A Textbook in Tribology, Boca Raton: CRC Press, 1996.
P. J. Blau, Friction, Lubrication, and Wear Technology, Materials Park: ASM International, 1992.
M. B. Peterson and W. O. Winer, Eds., Wear Control Handbook, New York: ASME Press, 1980.
Czichos, Tribology: A Systems Approach to the Science and Technology of Friction, Lubrication and Wear, Amsterdam: Elsevier, 1978.
A. Williams, Engineering Tribology, Cambridge: Cambridge University Press, 2005.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2025 Tiba Jamal Ahmed
This work is licensed under a Creative Commons Attribution 4.0 International License.